TC4钛合金微弧氧化膜结构对化学镀Ni-P镀层结合性能的影响

冯长杰 王琦 周雅 赵晴 杜楠

冯长杰, 王琦, 周雅, 赵晴, 杜楠. TC4钛合金微弧氧化膜结构对化学镀Ni-P镀层结合性能的影响[J]. 航空材料学报, 2011, 31(5): 40-46.
引用本文: 冯长杰, 王琦, 周雅, 赵晴, 杜楠. TC4钛合金微弧氧化膜结构对化学镀Ni-P镀层结合性能的影响[J]. 航空材料学报, 2011, 31(5): 40-46.
FENG Chang-jie, WANG Qi, ZHOU Ya, ZHAO Qing, DU Nan. Effects of Microstructures of Micro-arc Oxidation Films from TC4 Alloy on Adhesion Property of Electroless Ni-P Platings[J]. Journal of Aeronautical Materials, 2011, 31(5): 40-46.
Citation: FENG Chang-jie, WANG Qi, ZHOU Ya, ZHAO Qing, DU Nan. Effects of Microstructures of Micro-arc Oxidation Films from TC4 Alloy on Adhesion Property of Electroless Ni-P Platings[J]. Journal of Aeronautical Materials, 2011, 31(5): 40-46.

TC4钛合金微弧氧化膜结构对化学镀Ni-P镀层结合性能的影响

基金项目: 

航空科学基金(2009EF56020)

详细信息
    作者简介:

    冯长杰(1977- ),男,博士,副教授,主要从事表面防护涂层技术研究,(E-mail)13970051721@126.com.

  • 中图分类号: TG146.2

Effects of Microstructures of Micro-arc Oxidation Films from TC4 Alloy on Adhesion Property of Electroless Ni-P Platings

  • 摘要: 在TC4钛合金上制备微弧氧化不同时间的氧化膜,然后进行化学镀N i-P镀层,利用SEM、涂层附着力自动划痕仪和热震试验,研究不同微弧氧化膜结构对钛合金化学镀N i-P镀层结合性能的影响.结果表明:随着微弧氧化时间的增加,微弧氧化膜表面的粗糙度增大,表面微孔逐渐变大,孔口先变成敞开形式然后慢慢缩合,最后变成凹槽状.微弧氧化时间由3min增加至15min,化学镀N i-P镀层与微弧氧化膜的结合性能逐渐降低,临界载荷由21.5N减少至8.5N,且化学镀层表面划痕特征由裂纹向镀层剥落发展.微弧氧化时间由15min增加至60min,化学镀N i-P镀层与微弧氧化膜的结合性能逐渐增加,临界载荷由8.5N增加至大于40N.热震试验结果表明,微弧氧化3min,7min,15min的试样热震1次时,化学镀N i-P镀层发生严重的剥落,且在冷却过程中化学镀镍层剥落的顺序为15min,7min,3min的试样,30min的试样热震2次剥落,60min的试样热震28次才剥落,与划痕实验的结果一致.建立了不同微弧氧化时间,TC4钛合金微弧氧化膜的结构模型,讨论了不同微弧氧化膜结构与化学镀镍层的结合强度.

     

  • [1] 赵永庆,奚正平,曲恒磊.我国航空用钛合金材料研究现状[J].航空材料学报,2003,23(增刊):215-219.
    [2] 林翠,刘枫,赵晴,等.氢氟酸-硝酸体系中TC4钛合金的腐蚀行为[J].失效分析与预防2008,10(2):11-15.
    [3] BISWAS,Amit MAJUMDAR Jyotsna Dutta.Surface characterization and mechanical property evaluation of thermally oxidized Ti-6Al-4V[J].Materials Characterization,2009,60(6):513-518.
    [4] USTEL Fatih,ZEYTIN Sakin.Growth morphology and phase anslysis of titanium-based coating produced by thermo chemical method[J].Vacuum,2006,81(3):360-365.
    [5] 刘洪涛,邓长城.钛合金镀镍在航空航天工业中应用的可行性研究[J].功能材料,2010,41(2):249-252.
    [6] TSIPAS Sophia A,VáZQUEZ-ALCáZAR Maria R,et al.Boride coatings obtained by pack cementation deposited on powder metallurgy and wrought Ti and Ti-6Al-4V[J].Surface and Coatings Technology,2010,205(7):2340-2347.
    [7] ZHOU Qing-Jun,ZHAO Jian-Qiang,NIE Fei,et al.The effect of hydrogen on friction and wear of Ni-P electroless coating[J].Wear,2009,266(7~8):10-813.
    [8] ALIREZAEI S,MONIRVAGHEFI S M,SALEHI M,et al.Wear behavior of Ni-P and Ni-P-Al2O3 electroless coatings[J].Wear,2007,262(7~8):978-985.
    [9] 刘艳辉,高景龙,邵忠财.钛合金化学镀Ni-P合金前处理工艺的研究[J].电镀与精饰,2008,30(12):35-27.
    [10] YEROKHIN A L,NIE X,LEYLAND A,et al.Plasma electrolysis for surface engineering[J].Surface and Coatings Technology,1999,122(2):73-93.
    [11] 李健学,张玉梅,吴国锋,等.钛微弧氧化表面处理对钛瓷结合强度的影响[J].稀有金属材料与工程,2008,37:495-498.
    [12] WEI Da-qing,ZHOU Yu,WANG Yuan-bin,et al.Structure and apatite formation of microarc oxidized TiO2-based films before and after alkali-treatment by various alkali concentrations[J].Surface and Coatings Technology,2008.202(20):5012-5019.
    [13] 王庆良,葛世荣,史兴岭.钛合金微弧氧化陶瓷层的结构研究[J].中国矿业大学学报,2008,37(4):462-466.
    [14] 蒙晓涓,李卫京,崔世海,等.Ti6Al4V合金微弧氧化陶瓷膜的组织结构研究[J].航空材料学报,2009,29(2):39-42.
    [15] 刘忠德,孙茂坚,付华,等.微弧氧化时间对Ti6Al4V合金表面生物薄膜的影响[J].江华大学学报,2010,31(2):160-164.
    [16] ZHANG Sam,SUN Deen,FU Yongqing,et al.Toughness measurement of thin films:a critical review[J].Surface and Coatings Technology,2005,198:74-84.
    [17] 刘俊,王鲁,程焕武,等.高速冲击载荷下SiC骨架/Zr基非晶合金复合材料断裂行为研究[J] 北京理工大学学报,2010,30(6):873-877.
    [18] CLARK D R.Interpenetrating phase composites[J].Journal of American Ceramic Society,1992,75(4):739-759.
    [19] 刘娜,王鲁,才鸿年,等.三维连通网状SiC陶瓷/Zr基非晶复合材料室温单轴压缩断裂行为[J].北京理工大学学报,2008,26(3):741-744.
    [20] 周泽翔,程海斌,薛理辉,等.改善化学镀层结合力的方法及其检测手段[J].材料导报,2006,20(2):79-87.
  • 加载中
计量
  • 文章访问数:  1373
  • HTML全文浏览量:  47
  • PDF下载量:  234
  • 被引次数: 0
出版历程
  • 刊出日期:  2011-10-01

目录

    /

    返回文章
    返回