Creep Behavior and Fracture Mechanism of HCR GH4169 Superalloy
-
摘要: 通过蠕变性能测试及组织形貌观察,研究了热连轧直接时效处理的GH4169镍基合金的蠕变行为和断裂机制.结果表明:热连轧GH4169镍基合金的组织结构由γ',γ"相和γ基体相组成,具有较小的晶粒尺寸,晶内存在高密度位错和孪晶.经直接时效后,合金中弥散分布的细小γ"相数量增加,及高密度位错引起的形变强化效果,是使合金在650℃/725MP条件下具有较长的蠕变寿命的主要原因;蠕变期间,合金的变形特征是孪晶变形和位错的双取向滑移;随着蠕变进行,位错的数量逐渐增加,并在晶界处引起应力集中,致使裂纹在晶界处萌生及扩展是合金的蠕变断裂机制.
-
关键词:
- 热连轧GH4169合金 /
- 直接时效 /
- 蠕变 /
- 断裂机制
Abstract: By means of the creep curves measurement and microstructure observation,the creep behavior and fracture mechanism of HCR + DA GH4169 nickel-base superalloy are investigated.Results show that microstructure of HCR GH4169 alloy consists of the γ',γ" phase and γ matrix,and possessing in the fine grains in which exists significant amount of dislocations and twinning.After direct aged treated.the quantities of the dispersed fine γ" phase increases and the alloy retains the effect of the deformed strenghtening during hot continuous rolling,which is thought to be the main cause of the alloy possessing a longer creep lifetime under the applied stress of 725 MPa at 650℃.During creep,the deformation features of the alloy are twining and double orientation slipping of the dislocations.As the creep goes on,significant amount of dislocations is plied up the regions near the boundaries to bring out the stress concentration,which results in the initiation and propagation of the micro-cracks along the boundaries up to rupture.-
Key words:
- GH4169 alloy /
- hot continuous rolling /
- direct aging /
- creep
-
[1] TIAN S G,LI Z R,ZHAO Z G,et al.Influence of direct aging treatment on creep behaviors of hot continuous rolled GH4169 superalloy,Warrendale,USA,TMS,2010,455-462. [2] 宁永权,姚泽坤,郭鸿镇,等.等温锻造对IN718合金组织和性能的影响[J].热加工工艺,2007,36(21):65-67. [3] MAX F,DUAN Z,SHI H J,et al.Fatigue and fracture behavior of nickel based superalloy Inconel 718 up to the very high cycle regime[J].Journal of Zhe Jiang University Science(A),2010,11(10):727-737. [4] RAO G A,KYMAR M,SRINIVAS M,et al.Effect of standard heat treatment on the microstructure and mechanical properties of hot isostatically pressed superalloy inconel 718[J].Materials Science and Engineering(A),355(2003):114-125. [5] TIAN S G,ZHAO Z G,LIU Y,et al.Misconstrue and creep behavior of casting and rolling GH4169 superalloy after long-term aged[J].Symposium on Extraction and Proceedings Division held at the TMS 2009,San Francisco,2009:353-359. [6] 孙永华,李龙,陈国胜,等.不同热处理工艺对GH4169合金组织与性能的影响[J].稀有金属材料与工程,2010,39,(增刊1),472-475. [7] 何玉怀,于慧臣,郭伟林,等.直接时效GH4169高温合金疲劳裂纹扩展性能试验[J].航空动力学报,2006,21(2):349-353. [8] 田素贵,赵忠刚,陈礼清,等.直接时效处理对热连轧GH4169合金蠕变行为的影响[J].航空材料学报,2010,30(5):14-18. [9] 刘芳,孙文儒,杨树林,等.Al含量对GH4169镍基合金组织及稳定性的影响[J].金属学报,2008,44(7):791-797. [10] 陈国胜,王庆增,张玩良,等.GH4169合金细晶棒材的连轧工艺及其组织与性能[J].材料工程,2010(4):18-21. [11] 干勇,田志凌,董瀚,等.中国材料工程大典,钢铁材料工程(上):第2卷[M].化工工业出版社,北京,2006,728. [12] TIAN S G,ZHAO Z G,LIU Y,et al.Creep behaviors of DA casting and rolling GH4169 superalloy[J].Rare Metal Materials And Engineering,2009,38(Suppl.3),20-23. -
点击查看大图
计量
- 文章访问数: 1371
- HTML全文浏览量: 65
- PDF下载量: 198
- 被引次数: 0
下载: