Investigation on Fatigue Crack Propagation Behavior of TC11 and TC4 Ti Alloys at Room Temperature and 400℃
-
摘要: TC11和TC4这两种变形对这两种钛合金室温和400℃的疲劳裂纹扩展试验结果及其特性进行了分析.试验结果显示,两种钛合金的室温疲劳裂纹扩展速率的数据比较集中,而400℃时的分散性比较大.通过对造成数据分散性的原因分析,认为以平均值为期望值的线性回归拟合方法会造成偏危险的估计,因此提出了以数据上边界为基础的Paris拟合方法.根据两种钛合金的室温和400℃时的数据,发现TC11的裂纹扩展速率比较低,具有较好的损伤容限性能.Abstract: The fatigue crack propagation behaviors of two brands titanium alloys,TC11 and TC4,are studied.Fatigue crack propagation rate tests at room temperature and 400℃ were carried out.Results of the tests indicate that the experimental data at 400℃ seems more scatter than data at room temperature for both Ti alloys,especially for TC11.The reason of data scatter is discussed.Because of the high data scatter,the linear regression based on the average expectation is no longer suitable.Thus the prediction is non-conservative because of the large deviation of crack propagation rates on the high rate side.A new data fitting policy based on high propagation rate points is proposed.It is found that at room temperature and 400℃,the crack propagation rate of TC11 is slower than TC4.Consequently TC11 is better than TC4 from the damage tolerance point of view.
-
Key words:
- titanium alloy /
- fatigue /
- crack propagation rate /
- data fitting.
-
[1] 毕中南,张麦仓,周世杰,等.TC11合金热变形特性及变形参数对组织的影响[J].航空制造技术,2009,(10):77-81. [2] 董洁,李渭清,冯永琦,等,锻造工艺对TC11饼材显微组织的影响[J].稀有金属快报,2006,25(11):26-31. [3] 李重河,朱明,王宁,等.钛合金在飞机上的应用[J].稀有金属,2009,33(1):84-91. [4] 中国航空材料手册 第2版[M].北京:中国标准出版社,2002. [5] Lucjan W1TEK,Crack propagation analysis of mechanically damaged compressor blades subjected to high cycle fatigue[J].Engineering Failure Analysis,2011,(18):1223-1232. [6] 赵福星.以耐久性和损伤容限为中心的现役发动机寿命控制方法[J].航空动力学报,2001,16(4):305-308. [7] 许鄂俊.缺陷、损伤、微裂纹对航空发动机构件服役总寿命及可靠性的影响[J].航空发动机,2003,29(2):11-15. [8] GB/T 6398-2000金属材料疲劳裂纹扩展速率试验方法[S].北京:中国标准出版社,2001. [9] HB 7680-2000金属材料高温疲劳裂纹扩展速率试验方法[S].北京:中国航空工业总公司第三○一研究所,2000. [10] PARIS PC,ERDOGAN F.A critical analysis of crack propagation laws[J].Trans ASME Series D,1963,85:528-35. -
点击查看大图
计量
- 文章访问数: 1394
- HTML全文浏览量: 36
- PDF下载量: 242
- 被引次数: 0
下载: