弧电流对电弧离子镀CrN硬质涂层组织性能的影响

郑陈超 陈康敏 张晓柠 黄燕 关庆丰 宫磊 孙超

郑陈超, 陈康敏, 张晓柠, 黄燕, 关庆丰, 宫磊, 孙超. 弧电流对电弧离子镀CrN硬质涂层组织性能的影响[J]. 航空材料学报, 2011, 31(4): 51-55.
引用本文: 郑陈超, 陈康敏, 张晓柠, 黄燕, 关庆丰, 宫磊, 孙超. 弧电流对电弧离子镀CrN硬质涂层组织性能的影响[J]. 航空材料学报, 2011, 31(4): 51-55.
ZHENG Chen-chao, CHEN Kang-min, ZHANG Xiao-ning, HUANG Yan, GUAN Qing-feng, GONG Lei, SUN Chao. Effect of Arc Current on Microstructure and Mechanical Properties of CrN Coatings Deposited by Arc Ion Plating[J]. Journal of Aeronautical Materials, 2011, 31(4): 51-55.
Citation: ZHENG Chen-chao, CHEN Kang-min, ZHANG Xiao-ning, HUANG Yan, GUAN Qing-feng, GONG Lei, SUN Chao. Effect of Arc Current on Microstructure and Mechanical Properties of CrN Coatings Deposited by Arc Ion Plating[J]. Journal of Aeronautical Materials, 2011, 31(4): 51-55.

弧电流对电弧离子镀CrN硬质涂层组织性能的影响

基金项目: 

江苏大学高级人才基金(07JDG032);江苏大学科技创新团队资助的课题

详细信息
    作者简介:

    郑陈超(1987—),男,硕士研究生,主要从事金属材料表面工程及材料微观结构研究,(E-mail)zccdsw45@sina.com.

    通讯作者:

    陈康敏,(E-mail)kmchen@ujs.edu.cn

  • 中图分类号: TB43

Effect of Arc Current on Microstructure and Mechanical Properties of CrN Coatings Deposited by Arc Ion Plating

  • 摘要: 采用电弧离子镀技术在钛合金表面制备CrN涂层,利用扫描电镜(SEM)、X射线衍射仪(XRD)以及透射电镜(TEM)分析了弧电流对涂层组织结构以及力学性能的影响。结果表明,随着弧电流的升高,涂层沉积速率增大,表面熔滴的数量及尺寸增大,表面平整度明显下降。不同弧电流条件下均沉积出CrN单相涂层。弧电流改变了粒子、离子的轰击作用,从而影响到涂层表面的能量状态,CrN涂层的择优生长由(111)变为(200),(220)。随着弧电流的增加,CrN涂层的硬度先增大后减小,而涂层与基材间的结合力以及涂层的摩擦系数逐渐增大。弧电流为65A时涂层生长具有较高的沉积速率和较低的沉积温度,可获得尺寸较小的涂层组织。

     

  • [1] SCHULZ H,BERGMANN E.Properties and applications of ion-plated coatings in the system Cr-C-N[J].Surface and Coatings Technology,1991,50:53-56.
    [2] BENIEN H,MAUSHART J,MEYER M,et al.D C magnetron sputtering of oxidation-resistant chromium and CrN films monitored by optical emission spectrometry[J].Matersci Eng(A),1991,139:126-131.
    [3] 唐宾,李咏梅,秦林,等.离子束增强沉积CrNx膜层及微动摩擦学性能研究[J].材料热处理学报,2005,26(3):58-60.
    [4] 郭军霞,陈秋龙.类金刚石碳膜的结构及其微动磨损行为[J].材料保护,2003,36(9):15-18.
    [5] PARK Jong Hyun,CHUNG Won Sub,CHO Young-Rae,et al.Synthesis and mechanical properties of Cr-Si-N coatings deposited by a hybrid system of arc ion plating and sputtering techniques[J].Surface & Coatings Technology,2004,188 ~189:425-430.
    [6] 赵晚成,马亚军,李生华.CrN活塞环薄膜的摩擦学性能[J].润滑与密封,2005,2:59-66.
    [7] SHIN S H,KIM M W,KANG M C,et al.Cutting performance of CaN and Cr-Si-N coated end-mill deposited by hybrid coating system for ultra-high speed micro machining[J].Surface & Coatings Technology,2008,202:5613-5616.
    [8] LEE D B,LEEA Y C,KWON S C.High temperature oxidation of a CaN coating deposited on a steel substrate by ion plating[J].Surface and Coatings Technology,2001,141:227-231.
    [9] ENSINGER W,KIUCHI M.Cubic nitrides of the sixth group of transition metals formed by nitrogen ion irradiation during metal condensation[J].Surface and Coatings Technology,1996,84:425-428.
    [10] BERTRAND G,SAVALL C,MEUNIER C.Properties of reactively RF magnetron-sputtered chromium nitride coatings[J].Surface and Coatings Technology,1997,96:323-329.
    [11] 张晓柠,陈康敏,郑陈超,等.脉冲偏压对电弧离子镀CrNx薄膜组织结构与性能的影响[J].航空材料学报,2010,30(5):73-77.
    [12] 陈康敏,张晓柠,郑陈超,等.氮气分压对电弧离子镀CrNx薄膜组织结构的影响[J].真空科学与技术学报,2010,30(6):662-666.
    [13] 陈康敏,关庆丰,潘励,等.电弧离子镀NiCoCrAlY涂层的透射电镜研究[J].真空科学与技术学报,2009,29(1):21-25.
  • 加载中
计量
  • 文章访问数:  1267
  • HTML全文浏览量:  14
  • PDF下载量:  252
  • 被引次数: 0
出版历程
  • 收稿日期:  2010-12-16
  • 修回日期:  2011-02-25
  • 刊出日期:  2011-08-01

目录

    /

    返回文章
    返回