高温合金异形件表面薄膜热电偶研制取得突破性进展

罗炳威 曹丽莉 罗飞 牟仁德 王长亮 陈柳 孙坤 徐毅 刘松 周海涛 马可欣 田青云 史继源

罗炳威,曹丽莉,罗飞,等. 高温合金异形件表面薄膜热电偶研制取得突破性进展[J]. 航空材料学报,2023,43(6):117-120 doi: 10.11868/j.issn.1005-5053.2023.000184
引用本文: 罗炳威,曹丽莉,罗飞,等. 高温合金异形件表面薄膜热电偶研制取得突破性进展[J]. 航空材料学报,2023,43(6):117-120 doi: 10.11868/j.issn.1005-5053.2023.000184
LUO Bingwei,CAO Lili,LUO Fei,et al. Breakthrough progress of thin-film thermocouple development on special-shaped superalloy surface[J]. Journal of Aeronautical Materials,2023,43(6):117-120 doi: 10.11868/j.issn.1005-5053.2023.000184
Citation: LUO Bingwei,CAO Lili,LUO Fei,et al. Breakthrough progress of thin-film thermocouple development on special-shaped superalloy surface[J]. Journal of Aeronautical Materials,2023,43(6):117-120 doi: 10.11868/j.issn.1005-5053.2023.000184

高温合金异形件表面薄膜热电偶研制取得突破性进展

doi: 10.11868/j.issn.1005-5053.2023.000184
基金项目: 中国航发自主创新基金(JK65200309);中国航发航材院创新基金
详细信息
    通讯作者:

    罗炳威(1986—),男,博士,高级工程师,主要从事薄膜热电偶技术研究工作,联系地址:北京市海淀区环山村8号(100095),E-mail: luobingwei@126.com

  • 中图分类号: TB332

Breakthrough progress of thin-film thermocouple development on special-shaped superalloy surface

  • 摘要: 在GH5188高温合金异形件表面制备了铂铱薄膜热电偶,并将薄膜热电偶放置于焰流台,测试高温合金异形件表面的瞬态温度。经过高温高速焰流灼烧四个循环,总测试时长达到8700 s后,铂铱薄膜热电偶仍可以稳定获取温度数据。这次实验的成功,说明铂铱薄膜热电偶向工程化应用迈出了重要一步。项目团队瞄准薄膜热电偶工程化应用,研究了薄膜制备技术、界面调控、集成制备及信号与系统等内容,突破了13项关键技术,实现了铂铱薄膜热电偶的工程应用。该项实验的突破使得国内在叶片模拟服役条件下具备测温能力。

     

  • 图  1  薄膜热电偶测温关键技术图

    Figure  1.  Key technology of thin-film thermocouple

    图  2  铂铱薄膜热电偶焰流台测试 (a)薄膜热电偶焰流试验图;(b)高温合金异形件上薄膜热电偶实物图;(c)热电偶测试温度随时间变化图

    Figure  2.  Pt/Ir thin film thermocouple simulate high temperature and speed fire test (a)picture of simulate high temperature and speed fire test;(b) picture of thin film thermocouple prepared on the special-shaped high temperature superalloy;(c)plot of test temperature of thermocouples as a function of time

  • [1] 朱海南,齐歆霞. 涡轮叶片气膜孔加工技术及其发展[J]. 航空制造技术,2011,54(12):71-74.

    ZHU H N,QI X X. Development of machining technology gas holes on turbine blades[J]. Aeronautical Manufacturing Technology,2011,54(12):71-74.
    [2] LI X Y,REN J,JIANG H D. Influence of different film cooling arrangements on endwall cooling[J]. International Journal of Heat and Mass Transfer,2016,102:348-359. doi: 10.1016/j.ijheatmasstransfer.2016.06.047
    [3] 黄漫国,李水敏,张梅菊,等. 高温薄膜热电偶典型制备工艺研究现状分析[J]. 测控技术,2022,41(11):42-46.

    HUANG M G,LI S M,ZHANG M J,et al. Analysis on research status of typical preparation technology of high temperature thin-film thermocouple[J]. Measurement & Control Technology,2022,41(11):42-46.
    [4] 徐毅,黄明镜,程新琦,等. 航空发动机涡轮叶片涂层热电偶测温技术[J]. 航空发动机,2021,47(1):91-95.

    XU Y,HUANG M J,CHENG X Q,et al. Coating thermocouple measurement technique of aeroengine turbine blade temperature[J]. Aeroengine,2021,47(1):91-95.
    [5] JI Z L,DUAN F L,XIE Z Y. Transient measurement of temperature distribution using thin film thermocouple array on turbine blade surface[J]. IEEE Sensors Journal,2021,21(1):207-212. doi: 10.1109/JSEN.2020.3015383
    [6] XIE J H,JIANG H C,ZHAO X H,et al. Fabrication and performances of high-temperature transient response ITO/In2O3 thin-film thermocouples [J]. J Mater Sci:Mater Electron,2023,34:339.
    [7] TIAN B,CHENG G,ZHANG Z,et al. Optimization on thermoelectric characteristics of indium tin oxide/indium oxide thin film thermocouples based on screen printing technology[J]. Review of Scientific Instruments,2021,92(10):105001. doi: 10.1063/5.0057148
    [8] LUO B W,CAO L L,MA K X,et al. Hierarchical iridium nanostructure-based thin films with high-temperature stability and oxidation resistance for thermocouples[J]. ACS Applied Nano Materials,2022,5(3):4187-4195. doi: 10.1021/acsanm.2c00123
    [9] MA K X,CAO L L,LUO F,et al. Highly oriented platinum/iridium thin films for high-temperature thermocouples with superior precision[J]. Physical Chemistry Chemical Physics,2022,24(10):6163-6168. doi: 10.1039/D1CP05196B
    [10] LUO B W,CAO L L,GAO H L,et al. Superior thermoelectric performance of robust column-layer ITO thin films tuning by profuse interfaces[J]. ACS Applied Materials & Interfaces,2022,14(31):36258-36267.
  • 加载中
图(2)
计量
  • 文章访问数:  100
  • HTML全文浏览量:  27
  • PDF下载量:  60
  • 被引次数: 0
出版历程
  • 收稿日期:  2023-10-24
  • 录用日期:  2023-10-04
  • 修回日期:  2023-11-20
  • 刊出日期:  2023-12-08

目录

    /

    返回文章
    返回

    《航空材料学报》关于谨防假冒期刊的郑重声明

    近期,有不法分子冒充《航空材料学报》期刊及官网,谎称提供论文发表服务,发布虚假约稿信息,骗取作者发表费用,为此,本编辑部郑重声明如下:

    1、http://www.hkclxb.cn 为假冒网站,与《航空材料学报》没有任何关系。我刊没有委托任何第三方机构或个人,代表我刊约稿或提供发表服务。

    2、《航空材料学报》为中文期刊,只接收中文文章投稿,目前不刊登英文文章。

    3. 本刊官网是http://jam.biam.ac.cn/,本刊的官方投稿方式为网上投稿(登录官网首页—作者投稿)。如有不明可电话咨询,联系电话是010-62496277。

    敬请广大读者和作者认真识别,谨防上当受骗。