THE STUDY ON THE STAINLESS STEEL WIRE REINFORCED ALUMINUM MATRIX COMPOSITE

Author information +

文章历史 +

摘要

本文采用560C、70MPa0.5小时真空热压工艺制得了外观晶质优良、纤维排列均匀、厚约1毫米的不锈钢丝/铝复合材料板,并对其机械性能、拉伸应力-应变特性以及拉伸断口形貌进了分析,认为不锈钢丝增强铝复合材料具有广阔的应用前景。

Abstract

One mm thick stainless steel reinforced aiuminum composite plates with good appearance and well distributed fiberes (wires) were made by hot pressing under the condition of 560 C. 70MPa. 0.5h. The mechanical properties. stress strain curve and fracture surface of the composite plates in tensile testing were analysed. It was considered that the stainless steel aluminum composites reinforced with fibers (wirss) had a wide application future.

导出引用

高山, 孙长义. 不锈钢丝增强铝复合材料研究[J]. 航空材料学报, 1993, 13(2): 20-25

Gao Shan, Sun Changyi. THE STUDY ON THE STAINLESS STEEL WIRE REINFORCED ALUMINUM MATRIX COMPOSITE[J]. Journal of Aeronautical Materials, 1993, 13(2): 20-25

参考文献

[2] 苏联金属基复合材料的进展〔二)《航空材料动态》1989.第I期.
苏联金属基复合材料的进展(一《航空材料动态》1989.第3期.
[3] 铝一钢系复合材料《国外轻金属》1980. No. 11P36.
[4] 任荣镇孙长义高山不锈钢丝/铝金属基夏合材料拉伸过程中声发射特性研究《材料工程》1990