通过对DD100单晶合金组织、断裂等方面的研究,探讨了影响单晶的断裂延性的因素。当DD100单晶合金中加入适量Hf元素后,单晶合金中无明显的疏松孔洞,γ/γ’共晶数量增加。发生瞬间断裂的不含Hf元素的试样中存在亚晶界、疏松孔洞以及γ/γ’共晶,但亚晶界的危害超过后两者。
Abstract
The microstructure and fracture of Ni-based single crystal DD100 and the factors of influencing the ductility of the alloy have been investigated. With an addition of Hf in DD100 alloy,no obvious porosities were found and the amount of γ/γ’ eutectic was increased. Sub-boundaries,porosities and γ/γ’ eutectics appear in the tensile specimens without containing Hf. It was found that the effect of sub-boundary on the properties was greater than the others.
关键词
镍基单晶高温合金 /
断裂 /
亚晶界
{{custom_keyword}} /
Key words
Ni-based single crys /
fracture /
sub-boundary
{{custom_keyword}} /
{{custom_sec.title}}
{{custom_sec.title}}
{{custom_sec.content}}
参考文献
Eggeler G,Dlouhy A.γ'-phase Cutting during High Temperature Shear Creep Deformation of CMSX-6 Superalloy Single Crystals.Phys Stat 501,1995,9(a):349
[2] Mayer C,Rahmel A,et al.Douhle Shear Creep Testlng of Superalloy Single Crystals at Temperature above 1000 C.Mater Sci and Eng,1995,A199:121-130
[3] Gobel M,RahmelA,et al.The Isothermal-Oxidation Behavior of Several Nickel-Base Single-Crystal Superalloys with and without Coatings.Oxid Met,1993,39:231
[4] Gobel M,Rahmel A,et al.The Cyclic-Oxldation Behavlor of Several Nickel-Base Single-Crystal Supera lloys without and with Coatings.Oxld Met,1994,41:271
[5] U .5 P4,721,540
[6] 蔡玉林,郑运荣.高温合金的金相研究,北京:国防工业出版社,1986.70
[7] 宋德玉,罗治平等.DD3单晶合金在不同温度下的拉伸断裂特征.第八届高温合金年会学术论文特辑,金属学报增刊,1995.S433~436
[8] 张源虎,曹鹏等.DD3单晶高温合金慢拉伸断裂行为的研究.航空材料学报,1994,14(4):8
[9] 郑运荣.Hf在铸造高温合金凝固过程中的作用.金属学报,1986,22:A119
[10] 张静华等.影响单晶Ni高温合金持久性能的因素.材料科学进展,1991,5(5):381
[11] Walston WS,Bernsteln I M,et al.The Role of the γ/γ' Eutectlc and Porosity on the Tenslle Behavior of a Single-Crystal Nickel-Base Superalloy.Metall Trans,1991,22A:1443
[12] 艾素华等.单晶镍基高温合金的蠕变断裂.金属学报,1992,28:A126
{{custom_fnGroup.title_cn}}
脚注
{{custom_fn.content}}