深氮化硬化钢的接触疲劳试验研究

  • 江志华;李志;佟小军;李志明
作者信息 +

Experimental Study of Contact Fatigue for Deep Nitrided Steel

  • JIANG Zhi-hua;LI Zhi;TONG Xiao-jun;LI Zhiming
Author information +
文章历史 +

摘要

对双真空32Cr3MoVE钢深氮化件进行接触疲劳试验研究和全面分析。结果表明,失效形貌呈典型的接触疲劳特征,两种疲劳裂纹形成模式同时存在。深氮化试件具有优良的硬度梯度和残余压应力分布,与渗碳件相比接触疲劳寿命提高3.3~4.5倍。

Abstract

The contact fatigue experiment study was carried out for VIM+VAR 32Cr3MoVE steel by deep nitriding.The results showed that failure morphology was of typical contact fatigue characteristics,and two modes of fatigue crack formation worked.The steel by deep nitriding possessed excellent microhardness gradient and favorable distribution of residual compressive stresses,and the contact fatigue life of nitrided steel under the given load showed a great improvement in relation to carburized 18CrNi4A steel.

关键词

接触疲劳寿命 / 失效形貌 / 硬度梯度 / 残余压应力

Key words

contact fatigue life / failure morphology / microhardness gradie / residual compressive

引用本文

导出引用
江志华;李志;佟小军;李志明. 深氮化硬化钢的接触疲劳试验研究[J]. 航空材料学报, 2006, 26(3): 303-304
JIANG Zhi-hua;LI Zhi;TONG Xiao-jun;LI Zhiming. Experimental Study of Contact Fatigue for Deep Nitrided Steel[J]. Journal of Aeronautical Materials, 2006, 26(3): 303-304

参考文献

GUAGLIANO M,RIVA E,GUIDETTI M.Contact fatigue failure analysis of shot-penned gears[J].Engineering Failure Analysis,2002 (9):147-158.
GIRISH D V,MAYURAM M M,KRISHNAMURTHY S.Influence of shot penning on the surface durability of thermomechanically treated En 24 steel spur gears[J].Tribology International,1997,30(12):865-870.
PDF(424 KB)

14

Accesses

0

Citation

Detail

段落导航
相关文章

/