定向凝固高温合金DZ4的动态再结晶行为研究

贾波; 李春光; 李运菊; 陶春虎

PDF(1006 KB)

航空材料学报 ›› 2009, Vol. 29 ›› Issue (1) : 43-46.

扫码查看或转发全文

论文

定向凝固高温合金DZ4的动态再结晶行为研究

作者信息 +

Research on Dynamic Recrystallization Behavior of Directionally Solidified DZ4 Superalloy

Author information +

文章历史 +

摘要

研究了定向凝固DZ4合金在高温静拉伸应力作用下的动态再结晶行为,重点研究了温度、应力及表面氧化等因素对DZ4合金动态再结晶行为的影响.结果表明,在一定大小的应力作用下,不带涂层的DZ4合金试样表面在800~950℃范围内会发生动态再结晶,且再结晶层厚度随着温度和应力的增高而增大;动态再结晶层均位于表面氧化层内.分析表明,表面氧化是DZ4合金发生表面动态再结晶的主要原因.试验结果同时表明,表面采用Al-Si渗层保护的定向凝固DZ4合金叶片在正常服役条件下不会发生再结晶.

Abstract

Research on dynamic recrystallization behavior of directionally solidified DZ4 superalloy bearing static tensile stress at high temperature was carried out.How the factors affect dynamic recrystallization behavior of DZ4 superalloy,including temperature,stress and surface oxidation is mainly researched.The results show that dynamic recrystallization will occur in oxide layer at surface of DZ4 specimens without coating at 800℃ to 950℃ and the depth of recrystallization zone increases with the increase of temperature and stress.Analysis shows that surface oxidation is main reason for surface dynamic recrystallization.Experiment results also show that dynamic recrystallization won't occur at surface of DZ4 superalloy blades with protective Al-Si coating at normal working conditions.

导出引用

贾波, 李春光, 李运菊, 陶春虎. 定向凝固高温合金DZ4的动态再结晶行为研究[J]. 航空材料学报, 2009, 29(1): 43-46

JIA Bo, LI Chun-guang, LI Yun-ju, TAO Chun-hu. Research on Dynamic Recrystallization Behavior of Directionally Solidified DZ4 Superalloy[J]. Journal of Aeronautical Materials, 2009, 29(1): 43-46

参考文献

张卫方,高威,赵爱国,等.定向凝固合金叶片的疲劳断裂分析[J].机械工程材料,2003,27(9):48-51.
陶春虎,张卫方,李运菊,等.定向凝固和单晶高温合金的再结晶[J].失效分析与预防,2006,1(4):1-9.
陶春虎,颜鸣皋,张卫方,等.定向凝固和单晶叶片的损伤与预防[J].材料工程,2003(增刊):15-20.
HE Sheng-chun,Zhang Tian-cang,ZHANG sheng,et al.Dynamic Recrystallization Process and Microstructure of P/M Superalloy FGH96 Inertia Friction Welding Joint[A].AWJT 2005[C].Dalian China.
TIAN Baohui.Christoph Lind and Erhard Schafler.etc.Evolution of microstructures during dynamic recrystallization and dynamic recovery in hot deformed Nimonic 80a[J].Materials Science and Engineering(A),2004,367:198-204.
谷月峰,林栋梁,单爱党,等.定向凝固Ni3Al合金高温变形后的显微组织特征[J].金属学报,1998,34(4):351-355.
谷月峰,林栋梁,单爱党,等.定向凝固Ni3Al合金高温变形行为的研究[J].金属学报,1996,32(11):1145.
H J McQueen.Development of dynamic recrystallization theory[J].Materials Science and Engineering(A),2004:387～389:203-208.
张静华,唐亚军,胡壮麒,等.定向凝固DZ38G合金的热疲劳性能及微观组织[J].金属学报(A),1998,24(8):254.