C/C复合材料抗烧蚀HfC涂层的制备

作者信息 +

Preparation of Anti-ablation HfC Coating on C/C Composite Material

Author information +
文章历史 +

摘要

采用液相先驱体转化法在C/C复合材料表面制备了抗烧蚀HfC涂层.用红外光谱分析先驱体溶液的结构,用XRD、SEM和EDS对涂层进行了分析和表征.结果表明:先驱体溶液中主要存在Hf-O-Hf结构和Hf-O-C链式结构,有利于HfC涂层的形成;经过1800℃热处理后多层膜被转变为HfC涂层,形成的涂层中主要为HfC和HfO2;单次涂覆不能有效的覆盖C/C复合材料,多次涂覆能够生成致密的HfC涂层;涂层的厚度约为几十微米,涂层界面不明显,在涂层和基体间有较大过渡层能够缓解界面应力和提高与基体间的结合强度,有效延长寿命.

Abstract

Anti-ablation HfC coating was prepared by liquid precursor conversion on the C/C composite material.The solution-derived precursor was studied by FT-IR.The HfC coating was characterized by XRD,SEM and EDS.The results showed the Hf-O-Hf and Hf-O-C bonds appeared in the solution-derived precursor.The coating was conversed into the HfC coating after heat treatment at 1800℃.The components of the coating were mostly HfC and HfO2.The C/C composite material was not covered with Single coating.The HfC coating was compact from multi-films.The thickness of the coating was about several tens micron.The interface was not obvious.The transition coating between body and coating can relax interface stress and improve integrate intensity.

关键词

HfC / 涂层 / C/C复合材料

Key words

HfC / coating / C/C composite materi

引用本文

导出引用
侯根良, 苏勋家, 王延斌, 周晓波. C/C复合材料抗烧蚀HfC涂层的制备[J]. 航空材料学报, 2009, 29(1): 77-80
HOU Gen-liang, SU Xun-jia, WANG Yan-bin, ZHOU Xiao-bo. Preparation of Anti-ablation HfC Coating on C/C Composite Material[J]. Journal of Aeronautical Materials, 2009, 29(1): 77-80

参考文献

刘军,熊翔,王建营,等.耐高温材料研究[J].宇航材料工艺,2005(1):6-9.
SACKS Michael D,WANG Chang-an,YANG Zhao-hui.Carbothermal reduction synthesis of nanocrystalline zirconium carbide and hafnium carbide powders using solution-derived precursors[J].Journal of Materials Science,2004,39:6057-6066.
韩杰才,胡平,张幸红,等.超高温材料的研究进展[J].固体火箭技术,2005,28(4):289-294.
李荣久.陶瓷-金属复合材料[M].北京:冶金工业出版社,1995:12.
何捍卫,周科朝,熊翔.C/C复合材料抗烧蚀Ta/C涂层的制备[J].稀有金属材料与工程,2004(5):490-493.
卢嘉德.固体火箭发动机复合材料技术的进展及其应用前景[J].固体火箭技术,2001.24(1):46-52.
李春华,黄可龙,李效东,等.聚碳硅烷先驱体转换法制备SiC涂层研究[J].材料科学与工艺,2005(4):222-224.
陆静娟,郭兴忠,杨辉.先驱体配比对薄膜结构与性能的影响[J].稀有金属材料与工程,2004(12):273-276.
相华,徐永东,张立同,等.液相先驱体转化法制备TaC抗烧蚀材料[J].无机材料学报,2006(7):893-898.
PREISS H.,SCHIERHORN E.,BRZEZINKA K.W.Synthesis of polymeric titanium and zirconium precursors and preparation of carbide fibers and films[J].Journal of Materials Science,1998,33:4697-4706.
翁诗甫.傅立叶红外光谱学[M].北京:化学工业出版社,2005:7.
PDF(591 KB)

35

Accesses

0

Citation

Detail

段落导航
相关文章

/