Law of Uniaxial Tensile Tests of Ultra-high Strength 300M Steel Treated by Quenching-partitioning(Q-P) Process

MA Shao-hai;LI Yong;WANG Chun-xu;HUANG Shun-zhe;HAN Shun;LIU Xian-min

Journal of Aeronautical Materials ›› 2014, Vol. 34 ›› Issue (3) : 42-47.

PDF(1797 KB)
PDF(1797 KB)
Journal of Aeronautical Materials ›› 2014, Vol. 34 ›› Issue (3) : 42-47. DOI: 10.11868/j.issn.1005-5053.2014.3.007

Law of Uniaxial Tensile Tests of Ultra-high Strength 300M Steel Treated by Quenching-partitioning(Q-P) Process

Author information +
History +

Abstract

The uniaxial tensile curves of 300M steel treated by Q-P process were measured. And the energy of the various tensile stages of 300M steel were analyzed. Influence of Q-P process on the properties and structures of 300M steel was studied by TEM,SEM and XRD. The results show that the strength of 300M steel treated by Q-P process decreases significantly apparently, and the elastic deformation energy Ee decreases, but the uniform plastic deformation energy Ep and the crack initiation energy Ee+Ep increase. The content of residual austenite can be raised to 15.62%, which exists between martensite lathes in film status and between prior austenite grain boundaries、lath packet boundaries in massive form. The phases of 300M steel treated by Q-P process consist of pre-formed lath martensite, fresh martensite, residual austenite and -carbide.Q-P process significantly improve crack initiation and propagation resistance of 300M steel, and extend the uniform plastic deformation stage of the material,and finally put off the necking creation.

Key words

Q-P process / 300M steel / ultra-high strength / martensite / residual austenite / crack initiation ene

Cite this article

Download Citations
MA Shao-hai, LI Yong, WANG Chun-xu, HUANG Shun-zhe, HAN Shun, LIU Xian-min. Law of Uniaxial Tensile Tests of Ultra-high Strength 300M Steel Treated by Quenching-partitioning(Q-P) Process[J]. Journal of Aeronautical Materials, 2014, 34(3): 42-47 https://doi.org/10.11868/j.issn.1005-5053.2014.3.007

References

SPEER J G, MATLOCK D K, DE COOMAN B C, et al. Carbon partitioning into austenite after martensite transformation[J]. Acta Materialia, 2003, 51(9):2611-2622.
SPEER J G, EDMONDS D V, RIZZO F C, et al. Partitioning of carbon from supersaturated plates of ferrite, with application to steel processing and fundamentals of the bainite transformation[J]. Current Opinion in Solid State and Materials Science, 2004, 8(3-4):219-237.
周澍, 张柯, 顾剑锋, 等. 淬火-碳分配-回火钢低温组织和性能的研究[J]. 材料热处理学报. 2012, 33(6): 30-34.(ZHOU S, ZHANG K, GU J F, et al. Research of low-temperature microstructure and properties of quenching-carbon partitioning-tempered steel[J]. Transactions of Materials and Heat Treatment. 2012, 33(6): 30-34.)
王存宇. 30GPa%级超高强度钢马奥组织钢研究[D]. 北京: 钢铁研究总院, 2010.
徐祖耀. 淬火-碳分配-回火(Q-P-T)工艺简介[J]. 金属热处理, 2009, 36(4):1-6.(XU Z Y. Description of quenching-carbon partitioning-tempering (Q-P-T) process[J]. Heat treatment of metals, 2009, 36(4):1-6.)
韩顺, 王春旭, 厉勇, 等. 提高Ni含量对300M钢组织和性能的影响[J]. 热加工工艺, 2012, 41(20):75-78.(HAN S, WANG C X, LI Y, et al. The influence of Ni content on microstructure and mechanical properties of 300M steel[J].Hot Working Technology, 2012, 41(20):75-78.)
戎咏华. 先进超高强度-高塑形Q-P-T钢[J]. 金属学报, 2011, 47(12):1483-1489.(RONG Y H. Advanced ultra high strength-high shaping Q-P-T steel[J]. Acta Metallurgica Sinica, 2011, 47(12):1483-1489.)
李智超, 刘鹏砚, 王明罡, 等. Ms点的碳当量计算法[J].辽宁工程技术大学学报, 1998, 17(3):293-295.(LI Z C, LIU P Y, WANG M G, et al. The carbon equivalent calculation method of Ms point.[J]. Journal of Liaoning Technical University, 1998, 17(3):293-295.)
王从曾. 材料性能学. 北京: 北京工业大学出版社, 2008.
束德林. 工程材料力学性能. 北京: 机械工业出版社, 2007.
惠卫军, 董瀚, 翁宇庆, 等. 回火温度对Cr-Mo-V系高强度钢力学性能的影响[J], 金属学报, 2002, 38(10):1009-1014.(HUI W J, DONG H, WENG Y Q, et al. The effect of tempering temperature on the mechanical properties of high strength Cr-Mo-V system steel[J], Acta Metallurgica Sinica, 2002, 38(10):1009-1014.)
EVANS P J, CRAWFORD L K, JOHNE A.Ironmaking and Steelmaking, 1979, 24(5).361.
PDF(1797 KB)

25

Accesses

0

Citation

Detail

Sections
Recommended

/